Description
Pursuing Transparency
The higher surface hardness remained the same and reduced the amount of photopolymerization initiator that causes yellowness to the extreme.
Nu:le Coat Liquid Clear (hereafter Clear) is clear even immediately after light curing, so it is difficult to affect the original color tone of dental restoration even when applied overglaze. Therefore, Clear can be used easily for whitening shades.
Pellet thickness (immediately after light curing) : 1.0 mm
Applied 2 layers of Nu:le Coat
Clear on TWiNY A0 crown.
Small Curing Strain
The combination of flexible polyfunctional monomers and tough cross-linkable monomers reduced curing strain.
Therefore, even if the applied layer become thicker because of overglaze, it is less likely to occur cracks or floated surface.
Thanks to the small curing strain, the inhibition of cracking and floated surface can be expected even when a lot of liquid has been applied to the pit and fissure or the junction.
Curing deformation after light curing (strain amount) is greatly reduced comparing the thickness before light curing (0.5 mm) .
Excellent Durability
In the evaluation of toothbrush abrasion test (50000 times) *1), it is equal to or more than that of polishing finish, and excellent abrasion resistance has been confirmed.
It is reported that plaque adherence is rapidly increase when the surface roughness exceeds 0.2 μm *2). However, the surface roughness of Nu:le Coat applied surface is less than 0.1 μm even after 50,000 times of toothbrush abrasion test.
*1) ISO14569-1, the ratio of toothpaste and water is 1:2, Load weight 2.0N
Brush stroke 50,000 times is equivalent to about 7 years if it is assumed to brush teeth twice a day and brush 10 times per tooth.
*2) Bollen. M. Et al. : Dental Mater, 13 (4) 258~269, 1997.
Low Viscosity and Easy Application
Nu:le Coat Liquid was pursued an optimal viscosity that is easy to apply. Thanks to low viscosity design, hard to remain traces of a brush and easy to apply thinly and evenly. Thin hard-coated layers of about 5μm can be created, allowing coating and characterization without loosing the surface structure of dental restorations.
And please use Gel type when thicker layers are necessary.
color
Wide Range of Color Line-up for Crown Characterizing
White, Gray, Brown, Yellow, Orange and Blue lineups allow for free characterization of crowns.
Shade plus
There are A plus, B plus, C plus, and D plus lineups that allow fine adjustment of the shade.
Gum Shades
There are also Gum shade line-up (Red, Pink and Black) for denture application or Gum expression.
Pre-treatment of PEEK before applying resin materials.
Super engineering plastics PEAK-based (PEEK, PEKK, etc. ) have attracted attention in recent years for their ability to mitigate impact on bone in implant cases. By the combination of Clear and Gel, composite resin (e.g., Luna-Wing) and hybrid composite resin (e.g., TWiNY) can be built up on PEEK frame.
For Both Dental Laboratory and Chairside Use
Nu:le Coat can be used not only for the finishing of resin-based dental restorations but also for regular maintenance of resin-based dental restorations that have lost their glaze.
For Laboratory Use
After shape modification
Roughen the surface
(Alumina Sandblast etc.)
Application of Nu:le Coat
(characterizing and glazing)
Light Curing
(60 sec. by LED CURE Master)
Completion
For Chairside Use
Filling composite
After light irradiation, shape
modification and roughening
the surface.
Application of Nu:le Coat
(glazing)
Light irradiation
*Light irradiators should have an output peak wavelength of 400±20 nm, and also should contain the purple LED
Completion
For Color types, shake the bottle well before use as the
colouring material may settle.
Please avoid using this product for occlusal parts where
pressure is applied.