Description
General Description
Resin Modified Glass lonomer Cement (RMGI} Luting possesses unique triple curing mechanisms of conventional acid-base glass ionomer reaction, methacrylate resin chemical curing and light curable on demand. It is radiopaque (equivalent of >2.0 mm of aluminum) to better observe the condition of the abutment teeth in the prosthesis, as two-part paste/paste RMGI luting cement material. RMGI Luting provides the common benefits typical of other glass ionomer materials, along with the dual cure two-part paste of greater convenience over the traditional powder/liquid luting systems. The filler content of this system is primarily a combination of traditional silane treated barium-boro-silicate glass filler and acid reactive fluoroaluminosilicate glass filler having a hybrid particle size range from about 0.01 up to about 3 micrometers. The combined inorganic filler loading is about 65% by weight, while the resin system has a combination of phosphate and other methacrylate resins which are not having any Bisphenol A, or BPA derivative resin and/or Bis-GMA resin.
This cement achieves sufficient bond strength to tooth structure without the need of an etchant or an adhesive. Excess cement can be easily removed by allowing the cement to reach its gel state either through self-curing or tack-curing.
Indication
Advantages
Technical Parameter
| Mixing Ratio (base:catalyst) | 1:01 |
| Working Time (minimum) | 1 minute 30 seconds |
| Intra-oral Setting Time (maximum, from initial mix) | 4 minutes 30 seconds |